Olefin Metathesis in Confinement: Towards Covalent Organic Framework Scaffolds for Increased Macrocyclization Selectivity
Graphical Abstract
A biomimetic confinement and precise spatial arrangement of catalysts in porous media can provide increased selectivity for reactions compared to homogeneous catalysis. Herein, a covalent organic framework for molecular heterogeneous olefin metathesis is presented that utilizes spatial confinement of substrates in its pores for a substrate-size dependent and increased macro(mono)cyclization selectivity.
Abstract
Covalent organic frameworks (COFs) offer vast structural and chemical diversity enabling a wide and growing range of applications. While COFs are well-established as heterogeneous catalysts, so far, their high and ordered porosity has scarcely been utilized to its full potential when it comes to spatially confined reactions in COF pores to alter the outcome of reactions. Here, we present a highly porous and crystalline, large-pore COF as catalytic support in α,ω-diene ring-closing metathesis reactions, leading to increased macrocyclization selectivity. COF pore-wall modification by immobilization of a Grubbs-Hoveyda-type catalyst via a mild silylation reaction provides a molecularly precise heterogeneous olefin metathesis catalyst. An increased macro(mono)cyclization (MMC) selectivity over oligomerization (O) for the heterogeneous COF-catalyst (MMC:O=1.35) of up to 51 % compared to the homogeneous catalyst (MMC:O=0.90) was observed along with a substrate-size dependency in selectivity, pointing to diffusion limitations induced by the pore confinement.
Introduction
Covalent organic frameworks (COFs) are 2D or 3D extended structures, which are defined by their covalent connectivity, porosity, and crystallinity, while consisting exclusively of light elements.1 The vast structural and chemical diversity of COFs and the possibility to tune their framework with atomic precision has put COFs in the spotlight for a variety of applications that benefit from precise framework design, including photocatalytic water splitting,2, 3 sensing,4 batteries,5 gas adsorption,6 or heterogeneous catalysis.7 With their ordered micro- and mesoporosity and large specific surface areas exposing a large number of functional or even active catalytic sites, COFs are among the most promising materials for molecular heterogeneous catalysis. Classical approaches to design COFs for heterogeneous catalysis utilizing this feature include incorporation of catalytic centers directly in the pore wall,8 pore surface engineering by molecular catalysts via a post-synthetic reactions,9 integration of monodisperse nanoparticles in the framework by pore templating, or embedding polymers into the pores to combine multiple catalytic centers.10, 11
However, despite the promise of COFs as versatile scaffolds for catalysis, examples for the exploitation of reaction-specific pore confinement effects during catalysis, such as the substrate- specific and size-selective Knoevenagel-reaction achieved for microporous COFs by Fang et al.,12 are still rare. Altering selectivity and reactivity of the catalyzed reaction by spatial confinement is an immensely successful principle used in nature by enzymes and enzyme-inspired artificial catalysis. Taking full advantage of the ordered structural porosity of COFs thus bodes well for a biomimetic approach to catalysis where the precise spatial arrangement of catalytic centers and substrates, as well as pore confinement is utilized to direct product selectivity.13
In this work, we present a large-pore imine-COF as a molecular heterogeneous catalyst to study the effect of spatial confinement on product selectivity during olefin metathesis reactions; in particular macro(mono)cyclization (MMC) selectivity by ring-closing metathesis (RCM) and back-biting depolymerization vs. acyclic diene metathesis (ADMET) oligomerization (O, Scheme 1).
Competing metathesis reactions of α,ω-dienes resulting in macro(mono)cycles and oligomerization products.
Olefin metathesis-based macrocyclization offers an important pathway to useful compounds for industrial or pharmaceutical chemistry,14 however, it still poses severe challenges. Oftentimes, only low MMC yields are achieved due to the competing oligomerization by ADMET, originating from a ring-chain equilibrium during catalysis and back-biting RCM.15, 16 The biomimetic approach to olefin metathesis reactions by spatial confinement in pores for increased selectivity towards MMC products was already successfully shown for mesoporous silica by Jee et al. and Ziegler et al.16, 17 Applying this biomimetic approach to a COFs system not only diversifies the scope of possible confinement effects and framework-catalyst-reactant interactions, but at the same time offers new opportunities for precise, substrate- and product-specific catalyst-framework designs due the high structural and chemical diversity of COFs.
Results and Discussion
For the study of olefin metathesis reactions under spatial confinement in COFs, the model system, dHP-TAB COF, was synthesized by the condensation of 4,4′-(6-(4-hydroxyphenyl)phenanthridine-3,8-diyl)bis(2,6-dimethoxybenzal-dehyde) (dHP) and 5′-(4-aminophenyl)-[1,1′:3′,1′′-terphenyl]-4,4′′-diamine (TAB) in a solvent mixture of 1,2-dichlorobenzene (oDCB) and n-butanol (3 : 7) with 3 M acetic acid (AcOH) as catalyst for 96 h at 100 °C (Figure 1, a). After isolation by filtration, the solid was washed with methanol and subsequently activated by supercritical CO2. The large-pore COF system was chosen to accommodate the bulky catalyst and substrates and prevent pore blocking during immobilization and catalysis. Methoxy groups incorporated in the COF act as non-covalent anchors to achieve better layer registry and thus high porosity and large, well-defined pore sizes for this framework.18
(a) Synthesis of dHP-TAB COF. (b) Immobilization of Ru catalyst on dHP-TAB by silylation to form Ru@dHP-TAB.
Imine formation during the initial COF synthesis was confirmed by FTIR analysis (Figure S7). The spectrum shows the absence of the prominent aldehyde C=O stretching band at 1674 cm−1 and amine N−H stretching bands at 3355 cm−1 and 3431 cm−1, corresponding to the starting materials, indicating full conversion into imine bonds. The new imine stretching band is mostly concealed as slight shoulder at around 1614 cm−1 of the strong aromatic C−C stretching bands at 1593 cm−1. The solid-state 13C nuclear magnetic resonance spectrum (CP-MAS ssNMR) confirms the successful condensation by showing the typical imine signal at 160.0 ppm and the absence of aldehyde signals (Figure S18).
Crystallinity of dHP-TAB COF was confirmed by X-ray powder diffraction (XRPD), with the pattern (Co-Kα1) displaying several well-resolved diffraction peaks at 2 θ=2.0°, 3.5°, 4.0°, 5.3°, 6.9°, 7.3°, 8.8°, 10.5° and a broadened stacking reflection centered around 28.5° (Figure 2).
Experimental XRPD pattern of dHP-TAB COF, Rietveld refinement,19 difference curve and positions of the Bragg reflections. Inset: Structure of the respective 
stacked dHP-TAB along the a and b axis after refinement.
The structure was modeled in P31c symmetry with an alternating nearly-eclipsed 
stacking order of the layers. This assumed model is based on previous findings for phenylphenanthridine based COFs and shows a good match when compared to the simulated patterns of an 
stacked model (Figure S10). [18] Rietveld refinement of the pattern with the assumed model yielded unit cell parameters (a=b=58.824 Å and c=7.3 Å) with a satisfying agreement factor (Rwp=7.10 %, Rp=4.88 %) (Figure 2).19
Porosity of dHP-TAB COF was investigated by nitrogen physisorption measurements at 77 K, showing a type-IV isotherm, which is typical for mesoporous systems. The Brunauer-Emmett-Teller surface area (SBET) was calculated to be 1702 m2 g−1 with a total pore volume of 2.12 cm3 g−1 at P/P0=0.95. The pore size distribution (PSD) was determined from the adsorption branch by quenched solid density functional theory (QSDFT) based on the carbon model for cylindrical pores. It shows a narrow PSD around 4.8 nm, which is in good agreement with the structure model and closely related, isoreticular COFs.18
Next, the molecular catalyst RuCl2(N-mesityl-N-(3-(trimethoxysilyl)prop-1-yl)-imidazol-2-ylidene)(CH-2-(2-PrO-C6H4)) (Ru) was immobilized in the framework via silylation, utilizing the incorporated hydroxyl groups of the protruding phenols as anchor points (Figure 1, b). The immobilization was performed at room temperature in high-boiling oDCB as solvent under reduced pressure. Performing the reaction under reduced pressure significantly increases the catalyst loading by removing the accruing methanol from the reaction mixture and driving the reaction towards the desired outcome, yielding the catalyst-loaded Ru@dHP-TAB COF. Inductively-coupled plasma optical emission spectroscopy (ICP-OES) of the washed and dried sample revealed a Ru-content of c(Ru)=42.3 μmol/g for Ru@dHP-TAB COF. This corresponds to a successful silylation of approximately 3.4 % of the hydroxyl groups contained in the COF or roughly one catalyst per pore at every tenth layer.
No changes in the FTIR spectra of Ru@dHP-TAB compared to the pristine COF are visible, which can be attributed to the comparatively low amounts of immobilized catalyst (Figure S8) and the XRPD pattern (Figure S9); transmission electron microscopy (TEM) images show a retention of crystallinity (Figure S26). Nitrogen sorption measurements reveal only a minimal reduction in surface area (SBET=1645 m2 g−1) and total pore volume (1.95 cm3 g−1 at P/P0=0.95) compared to dHP-TAB with nearly identical pore size distribution (Figure 3). The largely retained porosity suggests that no substantial fraction of pores was fully blocked during the immobilization.
Comparison of (a) nitrogen isotherms at 77 K (filled circles for adsorption, empty circles for desorption) and (b) pore size distribution obtained from the adsorption branch of dHP-TAB and Ru@dHP-TAB after immobilization of the catalyst.
To confirm the stability of the catalyst during immobilization and to gain knowledge of the catalyst‘s structure in the pore, X-ray absorption (XAS) measurements were performed. Spectra of Ru and Ru@dHP-TAB as solids and in solution/suspension (benzene), respectively, were recorded.
The obtained X-ray absorption near edge structure (XANES) spectra (Figure 4, a and Figure S19), providing information about the oxidation state of the Ru-metal center,20 show no differences in the edge energy for all four samples measured. A change in the electronic structure or oxidation state by immobilization in the COF can thus be excluded.
(a) XANES spectra of the homogeneous Ru complex in the solid state (red), solution (green), immobilized in the mesoporous COF in the solid state (yellow), as suspension in benzene (brown), as well as of the Ru(0) foil used for calibration (black). (b) Fourier-transformed EXAFS data of the four Ru complexes. Continuous line: experimental data, dotted line: fitted data.
Results of extended X-ray absorption fine structure (EXAFS) analysis, probing the local geometric structure around an X-ray absorbing atom of the Ru catalyst under homogeneous and immobilized conditions are shown in Figure 4, b.21 The corresponding first shell scattering paths combined with coordination numbers, bond distances and Debye-Waller factors, which describe the static and dynamic disorder in the coordination shell, are collected in Figure S21 and Table S7. The results of the structure analysis for all samples are in good agreement with the single-crystal structure of the Ru catalyst.16 In the solid immobilized sample Ru@dHP-TAB, the second Ru−C distance is slightly elongated compared to the pure Ru complex, and the coordination number of this shell is increased. Since the changes cannot be explained by major structural modifications, they are assigned to the effect of the immobilization, such as pore wall interactions. This conclusion is backed by the results for Ru@dHP-TAB in benzene, where the structural alterations are reversed, as identified by structural parameters very similar to those of Ru in solution. Based on these observations, it can be concluded that neither the dissolution of the homogeneous complex in benzene nor the immobilization in a mesoporous COF lead to significant changes of the complex structure, which stays intact after immobilization. Neither ligand dissociation nor an association can be observed.
After confirmation of the stability of the COF framework and its immobilized catalyst, olefin metathesis reactions were carried out to determine the catalytic efficiency and the effect of the spatial confinement on MMC:O product selectivity. For this purpose, olefin metathesis reactions of four substrates (Figure 5, a) differing in their hydrodynamic radius and polarity were performed with the homogeneous Ru complex (Figure 1, b) as well as with Ru@dHP-TAB. [16] The reactions were carried out under identical conditions at 50 °C for 16 h in C6D6 using 0.5-mol % of catalyst and a substrate concentration of 25 mM; results are summarized in Table 1.
(a) Substrates 1–4 used in this study and their respective hydrodynamic radii (red) acc. to Ziegler et al.[16] (b) Correlation between the hydrodynamic radii of the substrates and increase in macrocyclization selectivity (blue) and conversion rate for the homogeneous (green) and heterogeneous catalyst (orange). The average of three reactions with Ru@dHP-TAB are displayed.
Substrate |
Conversion after 16 h [%] |
MMC : O |
MMC Selectivity [%] |
|||
|---|---|---|---|---|---|---|
|
Ru |
Ru@ dHP-TAB[a] |
Ru |
Ru@ dHP-TAB[a] |
Ru |
Ru@ dHP-TAB[a] |
1 |
81 |
9 |
0.90 |
1.35 |
47 |
56 |
2 |
77 |
10 |
0.84 |
0.99 |
46 |
50 |
3 |
80 |
9 |
0.65 |
0.63 |
39 |
39 |
4 |
73 |
14 |
0.40 |
0.55 |
28 |
35 |
- [a] Average over three performed reactions.
Stability of the COF framework during catalysis conditions was confirmed by post-catalysis XRPD, nitrogen sorption, ICP-OES and TEM measurements of the isolated materials, showing the retention of crystallinity and porosity (Figure S11, S15, S28). While the framework remains intact, the formation of unstable Ru methylidene complexes occurring during the catalysis ultimately deactivates the immobilized catalyst and therefore prevents recyclability.
The immobilization significantly alters the productivity of the catalyst, reducing the overall conversion after 16 h reaction time from around 80 % to around 10 %. This reduction was consistent for all substrates, independent of their size. This drastically reduced productivity is attributed to diffusion limitations and catalyst decomposition occurring during the reaction. However, a size-dependent increase in selectivity MMC:O was found for the catalysis with Ru@dHP-TAB compared to Ru (Figure 5, b). For the smallest substrate 1 (8.81 Å), an increase of 51 % in the MMC:O ratio from 0.90 for Ru to 1.35 for Ru@dHP-TAB was found, corresponding to a 9 % increase in selectivity compared to the homogeneous catalyst system. Furthermore, a continuously reduced macro(mono)cyclization selectivity with increasing substrate size is observed. For substrate 4 (9.05 Å) with a very similar radius to 1 the MMC:O ratio is increased by 38 %.
The very similar increase in selectivity for 1 and 4 with almost identical size but different polarity suggests that the polarity of the substrate has little influence on the reaction outcome. For the second largest substrate 2 (10.64 Å) only 18 % are achieved and the largest substrate 3 (11.71 Å) shows the same selectivity when catalyzed by Ru@dHP-TAB compared to the homogeneous Ru. This considerable size effect is rationalized by the substrate diffusion limitation into the COF mesoporous pores with increasing hydrodynamic radius. In the case of larger substrates, the reaction is mostly catalyzed by catalyst bound on the outer surface and close to the pore openings, mimicking the homogeneous ring-chain equilibrium.15 Smaller substrates can diffuse more easily and penetrate into the COF pores more deeply, where pore confinement effects can take place, favoring RCM for the ring-chain equilibrium products of the reaction by suppressing the formation of higher oligomers.22, 23 This is likely due to the very large internal surface area of the highly porous COF material that offers enough “inner” pore surface area for this size selective confinement effect to take place and to alter the ring-chain equilibrium.
Conclusion
In summary, we have developed a phenylphenanthridine-based COF containing accessible hydroxyl-groups on its protruding phenyl groups that allowed the successful immobilization of a Hoveyda-Grubbs-type catalyst in its pores to study possible pore confinement effects on the MMC selectivity during olefin metathesis reactions. The structure and ordered porosity of large-pore dHP-TAB COF with a pore size of 4.8 nm, suitable to accommodate both the bulky molecular catalyst and nm-sized substrates, was ascertained by XRPD analysis and nitrogen sorption experiments. The Ru-catalyst was effectively immobilized by simple silylation on hydroxyl-anchor groups integrated quantitatively in the framework and the retention of the catalyst's structure upon immobilization was confirmed by XANES/EXAFS measurements. A set of four diene substrates for olefin metathesis reactions, differing in their hydrodynamic radius and polarity, were used to probe the pore confinement effect during the reaction. Our results reveal significant confinement effects, which enhance the macrocyclization over oligomerization selectivity in the pores as compared to the homogeneous reaction. A clear trend between substrate size and MMC:O selectivity was found and can be attributed to a size-related, slower diffusion of the larger substrates into the pores, thus reducing the efficiency of confinement effects for the larger substrates while enhancing it for the smaller ones. Our results point to the possibility of tailoring the selectivity of olefin metathesis and other size-sensitive catalytic reactions by adjusting the subtle interplay between the size and polarity of both the COF pores and the substrates used for catalysis.
Acknowledgements
This work was funded by the Deutsche Forschungsgemeinschaft (DFG, German Research Foundation – project number 358283783 – SFB 1333). Financial support by the Max Planck Society and by the Cluster of Excellence e-conversion (EXC 2089) and the Center for Nanoscience (CeNS) is gratefully acknowledged. We thank Igor Moudrakovski for the solid-state NMR measurement and Viola Duppel for the SEM and TEM images. PETRA III is kindly acknowledged for provision of beamtime at beamline P65. Open Access funding enabled and organized by Projekt DEAL.
Conflict of interest
The authors declare no conflict of interest.
Open Research
Data Availability Statement
The data that support the findings of this study are available from the corresponding author upon reasonable request.